Neodym jernbor, NdFeB, magneter og korrosionsbestandighed

2020-10-16
DetNdFeB magneterkræver en beskyttende belægning / overfladefinish for at minimere virkningerne af korrosion. Jern i strukturen kan "stole", hvilket forårsager en permanent strukturændring i NdFeB, hvilket resulterer i en permanent svækkelse af den magnetiske ydeevne - det værste tilfælde er et totalt tab af magnetisme.

A NdFeB magnet kept in dry conditions will not corrode and will retain its performance theoretically for ever (if not subjected to excessive heat, radiation or strong external magnetic fields). If the conditions are wet, it is recommended that alternative magnets be considered for use of that the magnet design try to protect the magnet from moisture (e.g. encasing, modified coatings such as zinc plus rubber, etc). Detplating / surface finish should be hermetic for best corrosion protection – scratched or damaged surfaced may render the affected region more prone to corrosion. Marine environments (salt sprays, sea water) are particularly corrosive and far from ideal for NdFeB. In critical applications where corrosion and magnet failure are unacceptable, magnets such as ferrite or SmCo may be more suitable. Please note that any claims that a NdFeB magnetvil ikke korrodere er vildledende. Det hævdes, at højere Hci-magneter modstår korrosion bedre, selvom de empiriske resultater ikke er så afgørende (en tendens, der antyder en forbedring i korrosionsbestandighed, findes, men det er ikke garanteret). Det er applikationen og det overordnede design, der bestemmer, hvor godt magneten fungerer i fugtige omgivelser.